Epoxy composite modifications influence on the energy activation’s of thermal destruction.

Abstract

Values of the activation energy of the thermal-oxidative breakdown (E) of modified epoxy composite materials were calculated based on thermogravimetric analysis and using the Broido method. It is established that the composites with the SFEK modifier in an amount of q = 0.10 pts·wt. are characterized by the highest values of activation energy (E = 144.5 kJ/mol) and composites with the modifier in an amount of q = 1.75 pts·wt. are characterized by the activation energy which is equal to E = 175.0 kJ/mol. This indicates a significant effect of the modifier on the epoxy composites activation energy. The results of the experiments point to the formation of relatively thermally stable intra- and intermolecular bonds, which proves the compaction of the macromolecule cross-linking in the epoxy composites. The latter, in turn, leads to an increase of thermal stability and, as a consequence, the durability of materials. На основі термогравіметричного аналізу та за допомогою методики Бройдо були розраховані значення енергії активації термоокислюючої деструкції (Е) модифікованих епоксикомпозитних матеріалів. Встановлено, що найбільшими значеннями енергії активації (E = 144,5 кДж/моль) характеризуються композити з модифікатором СФЕК в кількості q = 0,10 мас.ч., а також композити з модифікатором в кількості q = 1,75 мас.ч., енергія активації яких дорівнює E = 175,0 кДж/моль. Це свідчить про значний вплив модифікатора на енергію активації епоксидних композитів. Результати експерименту також вказують на формування відносно термостійких внутрішньо- та міжмолекулярних зв’язків, що свідчить про ущільнення зшивання макромолекул епоксикомпозитів. Останнє що призводить до збільшення термостійкості і, як наслідок, довговічності матеріалів.